Anping Chuangye Metal Wire Mesh Co., Ltd>>Test Report
NO. Test items Technical Requirements Results
Detection Value Single conclusion
1.0 Grid solder jointŁ¬tensile strength, N 4.0 1320 6142 qualified
2.0 quality of anti-corrosion coating layer \ 6142 \
2.1 The average thickness of coatingŁ¬mm Column 0.4-0.8 0.54 qualified
Mesh Panel 0.49
2.2 Minimum thickness of coatingŁ¬mm Column 0.4 0.51 qualified
Mesh Panel 0.47
2.3 Sharing of coating thicknessmm Column 0.1 0.08 qualified
Mesh Panel 0.03
2.4 Coating Adhesion Column Coating and the substrate should be closely integrated with the planning grid method after the coating does not peel test meet the requirements qualified
Mesh Panel meet the requirements
2.5 Low-temperature impact resistance properties of coating Temperature of -40, a high degree of 1m, with the 1kg heavy ball impact specimen, the specimen surface without cracking phenomenon. meet the requirements qualified
2.6 Flame retardant coating Samples with the fire burning for five minutes, the specimen should not be burning, no burning or open flame to help undo, the burning sample should be immediately extinguished meet the requirements qualified
2.7 Chemical corrosion resistance coating \ \ \
2.7.1 Acid solution immersion At room temperature with 30% chemically pure h2so4 soaked in 720 hours, the coating surface, there should not be softening, wrinkles, blistering, cracking or surface edges are solutions such as the use of flaws. See The Center weathering test report See The Center weathering test report
2.7.2 Alkali solution immersion At room temperature with 10% chemically pure h2so4 soaked in 720 hours, the coating surface, there should not be softening, wrinkles, blistering, cracking or surface edges are solutions such as the use of flaws. See The Center weathering test report See The Center weathering test report
2.7.3 Soaked in salt solution At room temperature with 3% chemically pure h2so4 soaked in 720 hours, the coating surface, there should not be softening, wrinkles, blistering, cracking or surface edges are solutions such as the use of flaws. See The Center weathering test report See The Center weathering test report
3.0 Weathering Performance Weathering test is completed (cumulative acceptance of radiation energy> 3.5x106kj/m2), the specimen should be no significant discoloration, cracks, nicks, dents, bubbles, erosion, peeling, chalking or deformation, should not appear from any side The contraction of more than 1mm. See The Center weathering test report See The Center weathering test report
Anping Chuangye Metal Wire Mesh Co., Ltd .|Galvanized Welded Mesh Panel|Black Welded Mesh panel|Thread Welded wire mesh|PVC Coated Welded Mesh Panel|Wire Mesh Fence|Iron Wire
Copyright:Anping Chuangye Metal Wire Mesh Co., Ltd . Add:Xutuan Industrial Zone , Anping,Hebei, China Tel:+86-318-7682599
Fax:+86-318-7683599 URL:www.weldedpanel.com